Single-component thixotropic polyurethane adhesive with a paste-like consistency, hardens by reacting with moisture to form a resistant elastomer - excellent adhesive properties and high mechanical strength values - meets the low flame propagation standards defined by the International Maritime Organisation (IMO) - elastic, paintable, excellent filling capacity, able to withstand high dynamic stresses, dampens vibrations, non-corrosive, non-conductive - suitable for bonding metals, in particular aluminium (including anodised components), primed and painted metals (two-component systems), ceramic or plastic materials such as fibreglass, ABS, etc.
Chemical base: 1-C polyurethane
Colour (CQP1) 001-1) white RAL 1005
Curing mechanism atmospheric humidity
Density (uncured) (CQP 006-4) approx. 1.3 kg/l
Non-flowing properties (thixotropy) excellent
Application temperature from +10°C to +40°C
Dust-free time (CQP 019-1) approx. 40 min
Open time (CQP 526-1) approx. 30 min
Volumetric shrinkage (CQP 014-1) approx. 2%
Shore A hardness (CQP 023-1 / ISO 868) approx. 50
Tensile strength (CQP 036-1 / ISO 37) approx. 3 MPa
Elongation at break (CQP 036-1 / ISO 37) approx. 300%
Tear resistance (CQP 045-1 / ISO 34) approx. 8 N/mm
Shear strength (CQP 046-1 / ISO 4587) approx. 2.0 MPa
Glass transition temperature (CQP 509-1 / ISO 4663) Approximately -40°C
Electrical resistivity (CQP 079-2 / ASTM D 257-99) Approximately 5 x 10 9Ω·cm
Service temperature (CQP 513-1) -40°C to +90°C
short term 4 hours +120°C, 1 hour 140°C
Stability (storage at T < +25°C) (CQP 016-1) 12 months